Stainless Steel 316Ti Round Bars

Get a Price/Quote

Stainless Steel 316Ti Round Bars Specification

Corrosion Resistant
Excellent, especially against chloride environments

Hardness
HRB 95 max

Material Composition %
Cr 16-18%, Ni 10-14%, Mo 2-3%, Ti 0.5% max, Fe balance

Size
Standard and custom lengths available

Recyclable
Yes

Coating Type
Uncoated / As Rolled

Heat Resistance
Up to 870C continuous

Product Form
Bar

Tensile Strength
Min 515 MPa

Diameter
3 mm to 250 mm

Product Name
Stainless Steel 316Ti Round Bars

Steel Type
Stainless Steel

Steel Product Type
Round Bar

Grade
316Ti

Thickness
Ranges from 3 mm and above

Shape
Round

Steel Standard
ASTM A276, ASTM A479

Surface
Bright, Polished, Black

Composition
Cr-Ni-Mo-Ti Stainless Steel

Application
Construction, Chemical Processing, Marine Engineering, Oil & Gas Industry

Dimension (L*W*H)
Custom sizes available, typically as per customer specification

Weight
Varies as per dimension and length

Color
Silver / Metallic

Material Grade
316Ti

Finish Type
Polished / Bright / Black

Usage
Structural, Machined Parts, Fasteners, Shafts, Pipelines

About Stainless Steel 316Ti Round Bars

What Are Specification Stainless Steel 316Ti Round Bars?

Standard	ASTM A276 / A479, ASME SA276 / A479
Round Bar Size	3mm~ 800mm
Square Bar Size	4mm* 4mm ~100mm* 100mm
Flat Bar Size	2mm ~ 100mm
Hex Bar Size	2mm ~ 100mm
Angle Size	3mm* 20mm* 20mm~ 12mm* 100mm* 100mm
Thickness	50 mm to 6000 mm Long
Length	1 To 6 Meters, Custom Cut Length
Form	Round, Square, Hex(A/F), Rectangle, Billet, Ingot, Forging Etc

Equivalent material Of Stainless Steel 316Ti Round Bars?

STANDARD	WERKSTOFF NR.	UNS	JIS	BS	GOST	AFNOR	EN
SS 316Ti	1.4571	S31635	SUS 316Ti	320S31	08Ch17N13M2T	Z6CNDT17123	X6CrNiMoTi17-12-2

Chemical Composition Of Stainless Steel 316Ti Round Bars?

Grade	C	Mn	Si	P	S	Cr	Mo	Ni	N
SS 316Ti	0.08 max	2 max	0.75 max	0.045 max	0.030 max	16.00 18.00	2.00 3.00	10.00 14.00	68.395 min

Mechanical Properties Of Stainless Steel 316Ti Round Bars?

Density	Melting Point	Tensile Strength	Yield Strength (0.2%Offset)	Elongation
8.0 g/cm3	1399 C (2550 F)	Psi 75000 , MPa 515	Psi 30000 , MPa 205	35 %

Superior Corrosion Resistance

316Ti round bars excel in harsh environments due to their enhanced corrosion resistance, especially in chloride-rich or marine applications. The presence of molybdenum and titanium stabilisation ensures longevity and structural integrity, making them the preferred choice for industries such as chemical processing and marine engineering.

Tailored for High-Temperature Performance

These round bars are designed to resist oxidation and retain mechanical properties at elevated temperatures, with reliable heat resistance up to 870C for continuous service. This makes them particularly suitable for power plants and applications involving thermal stress.

Versatile Manufacturing and Customization

Available in both hot rolled and cold drawn variants, 316Ti bars come in a wide array of dimensions, finishes, and delivery conditions. Clients can request custom sizes and lengths, ensuring the product seamlessly integrates into any project specification.

FAQs of Stainless Steel 316Ti Round Bars:

Q: How are Stainless Steel 316Ti Round Bars manufactured?

A: 316Ti round bars are produced using both hot rolled and cold drawn techniques to achieve specific mechanical properties and surface finishes. After forming, the bars are annealed and may be pickled or polished according to application needs.

Q: What benefits does Titanium stabilisation offer in 316Ti bars?

A: Titanium stabilisation in 316Ti bars prevents carbide precipitation during welding or high-temperature exposure, enhancing resistance to intergranular corrosion and thus increasing service life in aggressive environments.

Q: When should I choose 316Ti round bars over standard 316?

A: Select 316Ti bars when extended service at elevated temperatures or in highly corrosive environments is needed, such as in chemical processing, power plants, and marine applications. The addition of titanium provides superior stability against corrosion and heat.

Q: Where can 316Ti round bars be used?

A: These bars are widely used in diverse industries including petrochemical, construction, food processing, marine engineering, oil and gas, and anywhere high corrosion resistance and strength are required.

Q: What is the typical lead time and packaging for 316Ti round bars?

A: Lead time generally ranges from 2 to 4 weeks, depending on order size and customization. Bars are packaged in export-worthy materials to ensure safe handling and transport globally.

Q: How do the mechanical properties of 316Ti round bars benefit structural applications?

A: With a minimum yield strength of 205 MPa and elongation above 35%, 316Ti bars combine strength with ductility, making them ideal for structural frameworks, load-bearing components, and precision machined parts.